Texture
|
Specification
|
Application
|
|
H0Cr21Ni10
|
Φ0.8-4.0
|
used for welding 304 steel and equipments like manufacturing chemical engineering and petroleum
|
|
2110Mn6
|
Φ1.2
|
|
|
307Si
|
Φ1.2
|
low Crack sensitivity due to high manganese content, applicable to rolled steels hard to weld like nonmagnetic steel, high manganese steel and wear-resistant steel of hardenability
|
|
2110Mn7Mo
|
Φ2.0
|
|
|
H00Cr21Ni10
|
Φ0.8-5.0
|
widely applied to petrochemical engineering, pressure vessel, food machinery,medical apparatus and instruments,fertilizer equipment,textile machinery,nuclear reactor and so on like welding 022Cr19Ni10(SUS 304L)
|
|
H0Cr21Ni10Nb
|
Φ1.0-2.5
|
|
|
H0Cr20Ni10Ti
|
Φ0.8-5.0
|
used for welding 19.5%Cr-9.5%Ni or similar alloy series stainless steel
|
|
2032Nb
|
Φ2.5
|
|
|
2313
|
Φ5.0
|
|
|
H1Cr24Ni13
|
Φ2.0-5.0
|
usually applied to weld stainless steel of the same type, stainless steel liner,dissimilar steel(06Cr19Ni10 and low carbon steel) and high-Cr steel and high-Mn steel,etc.
|
|
H1Cr24Ni13Nb
|
Φ1.2-2.5
|
|
|
2535Nb
|
Φ2.5
|
|
|
H00Cr24Ni13
|
Φ0.8-4.0
|
usually applied to stainless steel structure, ply steel and dissimilar steel,etc. of the same type produced by equipments like petrochemical engineering and synthetic fibre and so on
|
|
309LMo
|
Φ4.5
|
main composition is low C- 22Cr-12Ni-2Mo with all-position welding,welding operation is excellent with smooth wire feed,stable arc,beautiful form and few splash;deposited metal's mechanical property is stable with high percent of pass of X-Ray with excellently good anti-cracking ability due to adding Mo with low carbon,usually applied to welding carbon steel and stainless steel or martensite with bad tenacity and ferritic stainless steel and cast steel
|
|
H0Cr19Ni12Mo2
|
Φ1.0-3.2
|
usually used for petrochemical engineering and fertilizer equipment like welding 06Cr17Ni12Mo2(SUS 316)
|
|
H00Cr19Ni12Mo2
|
Φ0.8-5.0
|
ER316L is argon tungsten-arc welding stainless steel welding stick and equals TGS-316L produced in Japan for welding stainless steel containing Cr18Ni12Mo2 and stainless steel Cr18Ni12Mo2 with ultra-low carbon with good anti-cracking ability and anti-intergranular corrosion ability
|
|
316Si
|
Φ2.0-2.5
|
|
|
316LSi
|
Φ2.5-4.0
|
|
|
317L
|
Φ0.8-4.0
|
applied to weld stainless steel 18%Cr-12%Ni-2%Mo-N(SUS316LN,etc.) with low carbon and 19%Cr-13%Ni-3%Mo (SUS317L,etc.) with low carbon
|
|
2520Si
|
Φ2.5
|
|
|
H1Cr26Ni21
|
Φ1.0-4.0
|
usually for products of high temperature resistance such as high temperature furnace,coal Coker,etc. and also for multiple-bed surfacing and dissimilar steel
|
|
4Cr26Ni21Nb
|
Φ2.4-2.5
|
|
|
0Cr18Ni9
|
Φ0.8-4.0
|
|
|
1Cr18Ni9
|
Φ1.6
|
|
|
1Cr18Ni9Ti
|
Φ1.0-4.0
|
|
|
0Cr18Ni9Si2
|
Φ3.2
|
|
|
H0Cr14
|
Φ3.2
|
|
|
H1Cr14
|
Φ5.0
|
|
|
H00Cr14
|
Φ1.0-5.0
|
|
|
H00Cr14Ni6MoNb
|
Φ1.2
|
|
|
1625Mo6
|
Φ4.0
|
|
|
0Cr13
|
Φ1.6-3.2
|
|
|
00Cr13Ni5Mo
|
Φ1.35-5.0
|
|
|
3Cr13
|
Φ4.0
|
|
|
1Cr13
|
Φ1.6-3.2
|
|
|
2Cr13
|
Φ1.2-4.0
|
|
|
H1Cr17
|
Φ2.5-5.0
|
|
|
2Cr19Ni19Mo
|
Φ3.2-3.6
|
|
|
00Cr17Ni6Mo
|
Φ3.2-5.0
|
|
|
00Cr15Ni6MoNb
|
Φ2.0-3.2
|
|
|
13CrMoA
|
Φ2.5
|
|
|
1560
|
Φ2.0
|
|
|
2424
|
Φ2.4
|
|
|
309L-G
|
Φ1.0-1.2
|
|
|
308
|
Φ1.0
|
|
|
316
|
Φ1.0-3.2
|
|